All digital full text dissertation and theses from this website are authorized the copyright owners. These copyrighted full-text dissertation and theses can be only used for academic, research and non-commercial purposes. Users of this website can search, read, and print for personal usage. In respect of the Copyright Act of the Republic of China, please do not reproduce, distribute, change, or edit the content of these dissertations and theses without any permission. Please do not create any work based upon a pre-existing work by reproduction, Adaptation, Distribution or other means.
URN etd-0802105-162505 Statistics This thesis had been viewed 3588 times. Download 1985 times. Author Chun-Yuan Lue Author's Email Address email@example.com Department Materials Engineering Year 2004 Semester 2 Degree Master Type of Document Master's Thesis Language zh-TW.Big5 Chinese Page Count 75 Title Effects of GeO2 Addition On the Crystallization , Thermal Expansion, and Optical Transparency of Li2O-Al2O3-SiO2 Glass-Ceramics Keyword viscosity h-quartz s.s. expansion expansion h-quartz s.s. viscosity Abstract Li2O-Al2O3-SiO2 glass-ceramics containing nano-sized h-quartz s.s. crystals have optical transparency and ultra-low thermal-expansion coefficient. The objective of the thesis is to explore the effect of GeO2 addition on the crystallization and properties of Li2O-Al2O3-SiO2 glass-ceramics. It is expected that the viscosity of the parent glass will be reduced to profit glass shaping, and the IR transmission cut-off will be shifted to longer wavelength.
The experimental results indicated that viscosity of glass reduced with the increase in GeO2 content. A single h-quartz s.s. phase can be formed in the parent glass subjected to nucleation and crystallization thermal treatment. The crystal size increased with the increasing GeO2 content, affecting the optical transmission in visible region for the glass ceramics. Although the conditions of thermal treatment to gain good transmission (70%) is more narrow with the increase in GeO2 content, materials with the transmission closed to Zerodur® can still be obtained. The coefficient of thermal expansion of glasses and glass-ceramics that contain GeO2 was increased with respect to the GeO2 free composition. Addition of GeO2 is useless on extending the IR transmission cut-off wavelength for glasses and glass-ceramics.
Advisor Committee Jiin-Jyh Shyu - advisor
Ren-Der Jean - co-chair
Yi Hu - co-chair
Yung-I Chen - co-chair
Files Date of Defense 2005-06-23 Date of Submission 2005-08-02