All digital full text dissertation and theses from this website are authorized the copyright owners. These copyrighted full-text dissertation and theses can be only used for academic, research and non-commercial purposes. Users of this website can search, read, and print for personal usage. In respect of the Copyright Act of the Republic of China, please do not reproduce, distribute, change, or edit the content of these dissertations and theses without any permission. Please do not create any work based upon a pre-existing work by reproduction, Adaptation, Distribution or other means.
URN etd-0810108-142319 Statistics This thesis had been viewed 2787 times. Download 1284 times. Author Hao-Bang Ho Author's Email Address No Public. Department Chemical Engineering Year 2007 Semester 2 Degree Master Type of Document Master's Thesis Language zh-TW.Big5 Chinese Page Count 88 Title ELECTROLYTIC COLORING AFTER THE SECOND ANODIC TREATMENT OF ALUMINUM IN SULFURIC ACID SOLUTION WITH THE ADDITION OF 5-SULFOSALICYLIC ACID Keyword electrolytic coloring two-step anodic treatment addition of 5-sulfosalicylic acid addition of 5-sulfosalicylic acid two-step anodic treatment electrolytic coloring Abstract This study was carried out by means of the method of two-step anodic treatment in the sulfuric acid solution with the addition of 5-sulfosalicylic acid and then electrolytic coloring in cupric sulfate solution，it is expected that by adding 5-sulfosalicylic acid and technique of two-step anodic treatment, a dense and regular oxidizing film on aluminum can be obtained and that the optimum operating conditions for obtaining a blackest film are found out.
It is found that at the coloring after the anodic treatment by adding 5-ssa, the thickness of the anodized colored film would become thinner than that without the addition，but it would become thicker after two-step anodic treatment by adding 5-ssa. And，the hardness of anodic film from the addition of 5-ssa is larger than that without the addition, but it would become lower after two-step anodic treatment by adding 5-ssa. From SEM、 AFM and corrosion test of the anodic film after two-step anodic treatment by adding 5-ssa,it found out that the anodic film is more regular, smoother and denser, so it has the lowest △E after the coloring. It proves that more cupric ions deposit in the anodic film after two-step anodic treatment by adding 5-ssa.
At the anodic current density of 2 A/dm2 and the duration time of 20 minutes after two-step anodic treatment by adding 5-ssa, the best operating conditions of electrolytic coloring are：alternating current voltage：30V, and electrolytic coloring time：40 minutes, hence, the lowest △E value is 7.41. The average reflectivity, gloss, film thickness, hardness and corrosion rate are respectively 4.50%、8.6、10.2μm、591Hv and 3.1875E-9 Amp/cm2.
Advisor Committee Hsing-Hsiang Shih - advisor
Mu-Rong Yang - co-chair
Shyankay Jou - co-chair
Files Date of Defense 2008-07-31 Date of Submission 2008-08-12